融熔石英抛光片(JGS1 JGS2 Quartz glass)
光学石英玻璃片，能耐高温和高压等优点，是其他光学材料所无法替代的。石英玻璃具有良好的紫外透过性能；可见光和近红外光吸收极低，所以是生产光导纤维的基础材料。热膨胀系数极小，化学稳定性好，气泡、条纹、均匀性、双折射可与一般光学玻璃媲美，它是在恶劣场合下工作优选的光学材料。主要应用于：特种光源，光学仪器，光电子，军工，冶金，半导体，光通讯等领域。它能实验温度：1200度，软化温度为：1730度，具体参数如下：
The Optical quartz glass sheet has the advantages of high temperature and high pressure, which is irreplaceable by other optical materials. Quartz glass has good ultraviolet transmittance performance; Visible and near-infrared light absorption is extremely low, so it is the basic material for the production of optical fibers. The coefficient of thermal expansion is very small, the chemical stability is good, the bubbles, fringes, uniformity, and birefringence are comparable to the general optical glass, and it is the preferred optical material for working in harsh occasions. Mainly used in: special light source, optical instruments, optoelectronics, military industry, metallurgy, semiconductor, optical communication and other fields. It can be tested at 1200 degrees Celsius, softening temperature: 1730 degrees, the specific parameters are as follows:
1.(远紫外光学石英玻璃)对应牌号 JGS1
它是用高纯度氢氧熔化的光学石英玻璃，所以含有大量的羟基（2000ppm），具有优良的透紫外性能，特别是在短波紫外区，其透过性能远远地胜过所有其他玻璃，在185μm处的透过率可达90％，合成石英玻璃在2730nm处具有很强的吸收峰，无颗粒结构。是185—2500mμ波段范围内的优良光学材料。
It is an optical quartz glass（JGS1） with high purity hydrogen and oxygen melting, so it contains a large number of hydroxyl (2000ppm), with excellent ultraviolet transmission performance, especially in the short-wave ultraviolet region, its transmission performance is far better than all other glass, the transmittance at 185μm can reach 90%, synthetic quartz glass at 2730nm has a strong absorption peak,No granular structure.It is an excellent optical material in the range of 185-2500mμ band.
2.(紫外光学石英玻璃)对应牌号 JGS2
石英原料和氢氧焰生产的石英玻璃，含有几十ppm的金属杂质。在2730nm处有吸收峰（羟基含量100-200ppm），有条纹和颗粒结构。它是透过220—2500μm波段范围内的良好材料。
Quartz glass（JGS2） produced by quartz raw materials and hydrogen and oxygen flame contains tens of ppm of metal impurities.There is an absorption peak at 2730nm (hydroxyl content 100-200ppm), with stripes and granular structure.It is a good material for transmission in the 220-2500 μm band range.
本公司所能生产规格:
(Linan Optical company can produce specifications):
|
材料(Material) |
熔融石英(Quartz glass)(JGS1、JGS2、JGS2、康宁7980） |
|
规格尺寸(Specifications) |
Dia5.0~Dia300 5*5~200*200 |
|
面形精度(Surface Accuracy) |
根据客户要求制作 (Made according to customer requirements) |
|
公差(Tolerance) |
外形(shape):±0.05mm&+0/-0.10mm或其它(or other) 厚度(Thickness):±0.01mm或根据客户要求(or other) |
|
平行度(Parallelism) |
根据客户要求制作(Made according to customer requirements) |
|
表面光洁度(Scratch Dig) |
60/40，40/20，20/10，0/4 可根据客户要求制作 (Made according to customer requirements) |
石英玻璃光学常数(Optical constant of quartz glass):
|
各种光学石英玻璃所能达到的最高类别 (All kinds of optical quartz glass |
JGS-1 |
JGS-2 |
JGS-3 |
|
光谱特性 （Spectral characteristic Average transmittance） |
180-2500nm |
200-2500nm |
260-3500nm |
|
90% |
85% |
85% |
|
|
气泡类别（Bubble category） |
0 |
2 |
2 |
|
双折射（Birefringence） |
1-2 |
1-2 |
1-2 |
|
颗粒结构（Granular structure） |
1 |
2 |
2 |
|
条纹（Streak） |
1-2 |
1-2 |
2 |
|
均匀性（Homogeneity） |
1-2 |
2 |
2 |
|
荧光（Fluorescence） |
1 |
2 |
2 |
|
防辐射性能（Radiation resistance） |
不变色 non-discoloration |
轻微变色 Slight discoloration |
变色 discoloration |
石英玻璃物理性能(Physical properties of quartz glass):
|
表1.机 械 性 能（Table 1. Mechanical performance） |
标 准 值（Standard value） |
|
密度（Density） |
2.2g/cm3 |
|
抗压强度（Compressive strength） |
1100Mpa |
|
抗弯强度（Bending strength） |
67Mpa |
|
抗拉强度（Tensile strength） |
48Mpa |
|
泊松比μ（Poisson's ratio μ） |
0.14～0.17 |
|
杨氏模量E（Young's modulus E） |
72000Mpa |
|
刚性模量（Modulus of rigidity） |
31000Mpa |
|
莫氏硬度（Mohs hardness） |
5.5～6.5 |
|
表2.热 性 能（Table 2. Thermal properties） |
标 准 值（Standard value） |
|
变形点（Deformation point） |
1280℃ |
|
软化点（Softening point） |
1780℃ |
|
退火点（Annealing point） |
1250℃ |
|
比热(20～350℃)（Specific heat (20 ~ 350℃)） |
670J/kg.℃ |
|
热导率(20℃)（Thermal conductivity (20℃)） |
1.4W/m.℃ |
|
折射率（Refractive index） |
1.4585 |
|
热膨胀系数（Coefficient of thermal expansio） |
5.5×10-7cm/cm. ℃ |
|
热加工温度（Hot working temperature） |
1750～2050℃ |
|
短期使用温度（Short-term service temperature） |
1300℃ |
|
长期使用温度（Long-term service temperature） |
1100℃ |
我司各种常规石英产品(Our company's various conventional quartz products)：
 |
|
 |
 |
JGS1和是JGS2石英190~1100nm抛光白片对比曲线：
(Comparison curves of JGS1 and JGS2 quartz 190~1100nm polished white sheets)：